测定氧化诱导时间或温度:OIT和OOT

External influences such as UV radiation (light), temperature, atmospheric oxygen, atmospheric loads (e.g. impurities) or chemical/biological media lead to premature aging in organic materials, which might considerably influence their usage properties or might even lead to the failure of parts in which they are used as a component. The most common cause of chemical aging (e.g. chain degradation) is oxidation, which makes oxidation stability an important criterion for applications with oils, fats, lubricants, fuels or plastics. The oxidation stability can be determined via the Oxidation Induction Temperature / Oxidation Induction Time (OIT) by means of差分扫描量热法(DSC)在标准化程序中。

在实践中,使用了两种不同的方法:动态和等温oit测试。在动态技术中,在氧化条件下以限定的恒定加热速率加热样品直至反应开始。氧化感应温度液(也称为氧化生效温度OOT)与发生的放热DSC效应的外推开始温度相同。在等温物联网试验中,首先在保护气体下加热待研究的材料,然后在恒定温度下保持几分钟以建立平衡,随后暴露于氧气或空气的气氛中。从第一次接触氧气的时间跨度,直到氧化的开始称为氧化归纳时间oit

在ASTM D3895(聚乙烯),DIN EN 728(塑料管道)或ISO 11357-6(塑料)等国家和国际标准中详细描述了制备,实施和评估测量的程序。通常,使用盖子中具有多个穿孔的打开坩埚或坩埚。对于PE或PP等聚烯烃,更长的时间允许一个人得出结论,氧化稳定性更好,因此寿命更长。

您也可能对。。。有兴趣:

DSC 204.F1凤凰®

通过这种额外的差分扫描量热计(DSC)可以实现非常高的灵敏度和分辨率,该热量扫描量表(DSC)还具有自动样品更换器(ASC),温度调制(TM-DSC),基线优化(Beflat.®),校正热阻和时间常数(DSC校正),甚至耦合到QMS和FTIR以及光量测量法的UV延伸。

DSC 204 HP.凤凰®- 高压DSC

具有可选气体压力的DSC测量允许研究化学反应,汽化过程(ASTM E1782),吸附和解吸以及老化研究(ASTM E1858,ASTM D6186,ASTM E2009,ASTM D5483)进行额外的可能性。DSC 204 HP凤凰®,差示扫描量热计,理想地为这些应用配置。

DSC 3500.天狼星

DSC 3500.天狼星将紧凑性,稳健性和易用性与高检测灵敏度相结合,从而为食品,化妆品,聚合物,技术纺织品和有机无机材料等领域提供质量保证和失效分析的最佳条件。

DSC 214.Polyma.
  • 高性能
  • 智能测量
  • 自动评估
  • 创新鉴定
  • 易于样品制备
  • 独特的conc®平底锅